The influence of recommended mouthwashes against coronavirus disease 2019 on the shear bond strength of orthodontic brackets

INTRODUCTION

The emergence of the coronavirus disease 2019 (COVID-19) pandemic has evoked significant concern within global health systems, primarily due to the high transmissibility of the virus. It spreads easily through aerosols, droplets, or direct contact with respiratory secretions from infected individuals. Dental professionals face heightened vulnerability due to their proximity to patients’ respiratory tract openings during dental procedures^[1] and prolonged exposure to saliva containing a significant load of oral microbes, including the virus.^[2,3] Consequently, any dental intervention, particularly orthodontic procedures that may aerosolize contaminated saliva using handpieces and air-water syringes, has the potential to amplify airborne transmission of the virus greatly. Thus, dental professionals must implement comprehensive preventive protocols for infection control within dental settings.

Several oral antiseptic rinses have been recommended in recent studies for use before dental procedures to minimize the transmission of viruses. These include chlorhexidine gluconate, ethanol, essential oils, povidone-iodine (PVP-I), and hydrogen peroxide (H₂O₂) mouthwashes. While specific clinical studies on the efficacy of these mouthwashes in preventing cross-infection of COVID-19 are lacking, evidence suggests that rinses containing PVP-I and alcohol mouthwashes can reduce the viral load of severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) in saliva.^[4] The use of alcohol antiseptics for 30 s has been shown to reduce the viral load of human coronavirus by over 99.9%.^[5]

Similarly, rinsing with 0.2% PVP-I for 30 s has demonstrated the ability to decrease the infectivity of the SARS-CoV-2 virus to undetectable levels. In addition, PVP-I has been found to reduce the viral load in saliva and prevent the attachment of SARS-CoV-2 to oral and nasopharyngeal tissues.^[6,7] However, it is crucial to highlight that PVP-I should not be used in patients with abnormal thyroid function or a history of iodine allergy, as well as those with kidney disease, pregnancy, and children under the age of 6 years.

Exploring alternatives to PVP-I to mitigate these contraindications is essential to enable a broader population to access the benefits of preprocedural oral rinsing. H₂O₂ is acknowledged as a potent oxidizer with bactericidal and virucidal properties.^[8,9] Recommended by the American Dental Association as a preprocedural mouth rinse option, H₂O₂ holds promise against COVID-19 due to its susceptibility to oxidation. Its mechanism involves disrupting lipid membranes by generating oxygen free radicals. A recent systematic review highlighted the efficacy of 0.5% H₂O₂ in inactivating enveloped viruses, such as coronavirus 229E.^[10] The use of mouthwash containing 1% H₂O₂ has also been suggested to diminish the viral load of SARS-CoV-2 in saliva.^[11,12] In addition, H₂O₂ offers several advantages, including easy accessibility, low cost, and a well-established track record in dentistry.^[8,9]

The efficacy of fixed orthodontic treatment is contingent upon achieving optimal bond strength between orthodontic brackets and enamel. Effective bonding not only reduces bond failure rates but also contributes to shorter treatment durations and improved orthodontic mechanics. While previously published research highlights the potential prophylactic role of oral rinses in preventing viral disease transmission; there is a concern regarding their potential adverse effects on bond strength. However, limited research exists on the effects of recently recommended preoperative mouthwashes on the shear bond strength (SBS) of orthodontic brackets. Therefore, the objective of this study was to compare the effects of different mouthwashes recommended during the COVID-19 pandemic on the SBS of orthodontic brackets.

MATERIALS AND METHODS

Sample size calculation

Sample size calculation was conducted utilizing data from the pilot study, with a significance level (α) of 0.05, power (β) of 0.2, variance of means of 0.39, and effect size of 0.20. Accordingly, the study necessitated a sample size of 15 individuals in each group. A total of sixty teeth underwent testing to assess their SBS properties and adhesive remnant index (ARI) scoring [Figure 1].

Close

Figure 1:

Experimental flowchart. H₂O₂: Hydrogen peroxide, PVP-I: Povidone-Iodine.

Export to PPT

RESULTS

On comparing the three different mouth rinses with the control group, the artificial saliva group exhibited the highest mean SBS at 13.04 ± 3.55 MPa, followed by the H₂O₂ group with 12.65 ± 2.73 MPa, the PVP-I group with 12.56 ± 2.70 MPa, and the lowest SBS was observed in the alcohol group with 10.14 ± 1.91 MPa. Statistical analysis revealed significant differences in SBS among the various mouthwash groups (P < 0.05). The alcohol group demonstrated significantly lower SBS (P < 0.05) compared to the control group. However, no statistically significant difference was observed between the control, H₂O₂, and PVP-I groups [Figure 2].

Close

Figure 2:

Shear bond strength (Megapascal) of the bracket exposed to different mouthwashes. The alcohol group showed significantly lower SBS than the artificial saliva group (*P < 0.05). SBS: Shear Bond Strength; H₂O₂: Hydrogen Peroxide, PVP-I: Povidone-Iodine, CI: Confidence Interval.

Export to PPT

The distribution and percentages of ARI scores are detailed in [Table 1]. The Chi-square test revealed no significant differences among the four groups. In all groups, ARI scores of 1 and 2 were the most frequent. Interestingly, ARI score 3 was predominantly observed in the saliva group, while ARI score 0 was most prevalent in the alcohol group.

DISCUSSION

During the COVID-19 pandemic, various types of mouthwash, including PVP-I, H₂O₂, and alcohol, have been recommended to minimize viral transmission in dental settings. This study aimed to assess the impact of these pre-procedural mouthwashes on the SBS of orthodontic brackets. The findings revealed that the use of mouthwashes resulted in decreased SBS, with a significant reduction observed in the alcohol group. Consistent with previous in vitro studies,^[14,15] the SBS in the alcohol-containing mouthwash group was lower compared to other mouthwash groups. In addition, research by Lee et al.^[16] demonstrated that a 75% ethanol solution can reduce SBS by 30–50% compared to water-stored specimens, attributed to ethanol diffusion-induced microcracking in composite material.^[17] The ethanol content in mouth rinses has been observed to soften the composite resin used for bonding orthodontic brackets and dissolve its bisphenol A glycidyl methacrylate component, potentially explaining the observed decrease in SBS following the use of alcohol-containing mouth rinses.^[14,18] Despite the utilization of an alcohol mouthwash containing 21.6% ethanol in our study, it exhibited adverse effects on the SBS of orthodontic brackets. Therefore, there is a need for concern regarding the use of alcohol-containing mouthwashes in patients undergoing orthodontic treatment.

Despite the observed decrease in SBS following the use of preprocedural mouthwashes, our investigation revealed that the application of H₂O₂ and PVP-I did not have an adverse effect on the SBS of orthodontic brackets. This finding is consistent with the study conducted by Ghobadi et al.^[19] who suggested that H₂O₂ and PVP-I mouthwashes may serve as alternatives for orthodontic patients seeking antiviral properties against COVID-19 without compromising the SBS of metal orthodontic brackets. In contrast, previous studies have demonstrated that the use of 1.5% H₂O₂ and 0.2% PVP-I before bracket bonding leads to a reduction in SBS.^[20,21] They observed a thin hybrid layer with short resin tags in the H₂O₂ groups, while the PVP-I groups exhibited many gaps in the hybrid layer with diminished resin tag formation.^[20] These discrepancies in outcomes may be attributed to variations in testing protocols employed across studies, thereby influencing the observed results. In our study, brackets were bonded before exposure to H₂O₂ and PVP-I mouthwashes to simulate the rinsing process between orthodontic adjustment visits. This approach aimed to provide insights into the effects of these mouthwashes on SBS under conditions representative of clinical practice.

The success of fixed orthodontic treatment critically depends on achieving an optimal bond strength between orthodontic brackets and enamel. Excessive bond strength risks damaging enamel during debonding, while insufficient strength may lead to bracket detachment during treatment. Hence, determining the appropriate value of bond strength is essential to prevent these complications. Reynolds and von Fraunhofer^[22] proposed a SBS range of 6–8 MPa for clinical applicability, while Diedrich^[23] recommended a range of 5–10 MPa for orthodontic bracket placement. Our study demonstrated that the bond strength of all groups fell within this clinically acceptable range. Despite alcohol-containing mouthwashes causing a significant reduction in the SBS of orthodontic composites, this decrease remains within acceptable limits. Thus, the use of alcohol-containing mouthwashes could be deemed acceptable within defined parameters.

The ARI could serve as a valuable indicator of adhesion failure. When such failure occurs between the bracket and the adhesive material, it can potentially safeguard the enamel surface from damage during bracket debonding. However, this may prolong treatment duration as it necessitates additional time for the removal of residual adhesive. Conversely, if adhesion failure occurs between the enamel surface and the adhesive material, even minimal residual adhesive material can lead to enamel surface damage during bracket debonding. Our findings indicated that the ARI score of 0 was most prevalent in the alcohol mouthwash group, while other groups tended to have higher ARI scores, indicating more composite material remaining on the enamel surface after debonding. Although less adhesive remaining on the tooth surface after debonding may facilitate more efficient cleanup,^[24,25] it also poses a greater risk of tooth surface damage, including enamel crack and fracture. Therefore, a fracture occurring in the adhesive may be preferable to enamel failure, as it reduces the risk of damage to the tooth surface. However, it is important to note that the ARI does not necessarily correlate with the SBS value of the adhesive.^[26]

The strength of this study lies in its comprehensive comparative analysis of three distinct mouthwashes – an alcohol-containing mouthwash, H₂O₂, and PVP-I – and their effects on the SBS of orthodontic brackets within a uniform experimental framework. By evaluating these agents under standardized conditions, the study enables clinicians to make more informed decisions regarding preprocedural mouthwash selection. In addition, the exploration of alternatives to alcohol-based solutions broadens the scope of recommended antiviral agents in dental settings. This diversification is crucial for patients who are sensitive to alcohol and for practices aiming to minimize the use of alcohol-based products. The findings demonstrate that effective preprocedural mouthwashes can be used without compromising the integrity of orthodontic treatments, thereby achieving a critical balance between infection control and treatment efficacy during the pandemic.

While our current study provided valuable insights into the impact of preprocedural mouthwashes on orthodontic bracket bond strength, its primary limitation lies in the difficulty of comparing an in vitro investigation with clinical practice conditions. Factors such as temperature, moisture, and chemical interactions present in saliva can significantly influence the effects of mouth rinses on SBS. Saliva has the potential to dilute or buffer mouth rinse solutions, and the salivary pellicle may offer a protective effect. In addition, the absence of mechanical stresses from mastication and oral hygiene practices in vitro means that factors influencing bracket longevity and performance are not fully represented. ^[27,28] Recognizing these limitations is essential for the accurate interpretation of our findings and underscores the need for cautious application to clinical scenarios. Consequently, extensive clinical trials conducted over extended durations are necessary to fully evaluate the in vitro effects of preprocedural mouth rinses on bond strength and bracket failure rates in orthodontic patients. In addition, further investigations with varying bonding systems and different concentrations of mouthwashes would provide valuable insights.

CONCLUSION

The alcohol mouthwash showed the lowest SBS, indicating caution in its use during fixed orthodontic treatment due to its potential to compromise bond strength. Conversely, 1% H2O₂ and 0.5% PVP-I mouthwashes did not negatively affect the SBS of metal orthodontic brackets. This suggests that they could be viable alternatives for orthodontic patients seeking antiviral properties against COVID-19.